Achitèk Fib Avanse
- PA66 LGF40 entegre 40% fib vè long (10-12 mm) ak poliamid 66 matris nan teknoloji propriétaires pultrusion. Koòdone nan fib-rezin optimize reyalize 89% efikasite transfè estrès, depase konvansyonèl kout-fib konpoze nan rezistans fatig (10⁷ sik nan 70MPA)
Pèfòmans Enjenieri:
- Entegrite estriktirèl:296MPa fòs fleksib ak 8.9gpa modil, ideyal pou chaj-pote konpozan
- Tèmik andirans: 246 degree HDT @1.8MPa maintains dimensional stability under hood temperatures
- Estabilite chimik:Reziste ASTM #3 imèsyon lwil (ΔV<3% after 1000hrs)
Pwopriyete materyèl sètifye
| Posesyon | LFT-G®PA66 LGF40 | PA 66- SGF40 | PP-GF40 | Metòd tès |
|---|---|---|---|---|
| Fòs rupture | 195 MPA | 168 MPA | 160 MPa | ISO 527 |
| Charpy enpak (Notched) | 35 kJ/m² | 32 kJ/m² | 38 kJ/m² | ISO 179 |
| Koyefisyan friksyon | 0.15-0.25 | 0.30-0.40 | 0.35-0.45 | ASTM D1894 |
| Rating flanm dife | Ul94 v -0 | Hb | V0 | UL 94 |
Solisyon sistèm otomobil
Aplikasyon relatif
Pati Lojman Ponp Chimik
LFT-G®PA66 LGF granules konpoze
Tèminal estasyon plastik pati
Konpozan Powertrain
- Lwil ponp lwil ak 0. 05mm Tolerans chèn nan 150 degre
- Transmisyon parantèz pase 15g tès Vibration
E-Mobilite Sistèm
- 800V konektè batri ak CTI 600V Rating
- Charger Houseings Reyinyon IP67 Sele
Gid pwosesis teknik
Paramèt bòdi
| Paramèt | Optimal Range | Kontwòl kritik |
|---|---|---|
| Tanperati fonn | 293-310 degre | Anpeche degradasyon fib |
| Presyon piki | 80-120 MPA | Kenbe oryantasyon fib |
| Kondisyon siye | 4h@85 degre | Mwens pase oswa egal a 0. 18% imidite |
Espesifikasyon outillage
- Segondè kavite Polonè (ra mwens pase oswa egal a 0. 2μm) pou fini sifas
- Gates te demisyone ak L: T =1: 1 rapò