PP LGF30|30% long vè fib polypropylène|Jeni-klas konpoze
LFT-G®PP LGF30: Jeni-klas konpoze estriktirèl
Teknoloji Nwayo Materyèl
Sistèm ranfòsman fib
- 10mm e-vè fib ak ajan kouti silan (ECR-Glass 240Tex)
- Fiber length retention >88% (ISO 22314 Kontwòl Pwosesis)
- Optimize oryantasyon fib nan piki milti-pòtay
- Fòs lyezon interfacial: 32MPA (ASTM D2344)
- Distribisyon dyamèt fib: 12-15 μm (analiz SEM)
- Fib Volim fraksyon: 30% ± 2% (ASTM D3171)
Matris optimize
- High-koule PP kopolimè (MFR: 25g/10min @230 degre)
- Nivo grèf maleik anidrid: {{0}}. 6-1. 0 wt%
- Pake estabilizasyon UV: 0. 3% hals + 0. 2% antioksidan
- Absòpsyon imidite:<0.05% (ISO 62)
- Ajan Nucleating pou kristalize rapid
- Halogen-gratis flanm dife rezistan pake aditif
Espesifikasyon pèfòmans mekanik
Pwopriyete estatik
| Posesyon | Valè | Estanda |
|---|---|---|
| Fòs rupture | 121 MPa | ISO 527 |
| Modil Flexural | 5,800 MPa | ISO 178 |
| Fòs konpresiv | 95 MPa | ASTM D695 |
| Rapò Poisson an | 0.35 | ASTM E132 |
| Dite (Shore D) | 72 | ASTM D2240 |
Pwopriyete dinamik
- Charpy enpak Notched: 32 kJ/m² @23 degre
- Limit andirans fatig: 40mpa @10⁶ sik
- Modil ranpe: 3,200 MPa @1000h
- Mete pousantaj: 1.2mm³/km (ASTM G65)
- Koyefisyan friksyon: 0. 18
Tèmik & pèfòmans elektrik
Pwopriyete tèmik
- HDT @1.8MPa: 152 degree
- Kontinyèl itilize temp: -30 degre nan +120 degre
- CTE: 4.2 × 10⁻⁵/ degre
- Tèmik konduktivite: 0. 28 w/m · k
Pwopriyete elektrik
- Fòs dielèktrik: 22 kV/mm
- Rezistivite sifas: 1 × 10¹³ ω
- Konparatif endèks swiv: 400V